Study of Microstructure and Hot Deformation Behavior of Aluminum Nanocomposites Reinforced with SiC Nanoparticles, M.Sc. Thesis Sharif University of Technology ; Simchi, Abdolreza (Supervisor)
Abstract
Hot deformation behavior of Al-SiC nanocomposites was investigated in this study. Aluminum powders with mean size of 60 micron and SiC nanopowders (mean size of 45nm) in amounts of 1 and 2 volume percents, as reinforced part, were mixed and milled for 40 hours by planetary ball mill. After degassing at 450 oC for 1 hour, milled powders were pressed into Aluminum cans (in Argon atmosphere) and then hot extruded. Extrusion ratio was 1:14. High density billets (with 98% of theoretical density) were produced because of that high extrusion ratio. TEM microstructure studies showed that fine distribution of reinforcements and Aluminum Oxides obtained via this procedure. Hardness and Uniaxial...
Cataloging briefStudy of Microstructure and Hot Deformation Behavior of Aluminum Nanocomposites Reinforced with SiC Nanoparticles, M.Sc. Thesis Sharif University of Technology ; Simchi, Abdolreza (Supervisor)
Abstract
Hot deformation behavior of Al-SiC nanocomposites was investigated in this study. Aluminum powders with mean size of 60 micron and SiC nanopowders (mean size of 45nm) in amounts of 1 and 2 volume percents, as reinforced part, were mixed and milled for 40 hours by planetary ball mill. After degassing at 450 oC for 1 hour, milled powders were pressed into Aluminum cans (in Argon atmosphere) and then hot extruded. Extrusion ratio was 1:14. High density billets (with 98% of theoretical density) were produced because of that high extrusion ratio. TEM microstructure studies showed that fine distribution of reinforcements and Aluminum Oxides obtained via this procedure. Hardness and Uniaxial...
Find in contentBookmark
|
|