Evaluation Effects of Mo, Bi &Sn Biocides On the Anti-Fouling Paints, M.Sc. Thesis Sharif University of Technology ; Afshar, Abdollah (Supervisor)
Abstract
In this research Feasibility of application of oxide compounds of bismuth, molybdenum and tin as biocide was studied. So some epoxy paints with different ratio of these compounds were formulated. Afterward some tests were performed to assessment paints properties such as leaching rate, antifouling activity, adhesion, corrosion resistance and impact resistance. Results of leaching rate test showed that increase in the ratio of bismuth oxide from 10% to 60%, led to increase leaching rate from 0.029mg.day-1.cm-2 to 0.126mg.day-1.cm-2. beside that Microscopic results showed proved that the ratio of bismuth oxide in the cured coating is 25% of the paint formulate. In similar ratio of biocides,...
Cataloging briefEvaluation Effects of Mo, Bi &Sn Biocides On the Anti-Fouling Paints, M.Sc. Thesis Sharif University of Technology ; Afshar, Abdollah (Supervisor)
Abstract
In this research Feasibility of application of oxide compounds of bismuth, molybdenum and tin as biocide was studied. So some epoxy paints with different ratio of these compounds were formulated. Afterward some tests were performed to assessment paints properties such as leaching rate, antifouling activity, adhesion, corrosion resistance and impact resistance. Results of leaching rate test showed that increase in the ratio of bismuth oxide from 10% to 60%, led to increase leaching rate from 0.029mg.day-1.cm-2 to 0.126mg.day-1.cm-2. beside that Microscopic results showed proved that the ratio of bismuth oxide in the cured coating is 25% of the paint formulate. In similar ratio of biocides,...
Find in contentBookmark |
|