Mechanical Properties of Al2O3-ZrO2 Nanocomposites Fabricated by Gelcasting, M.Sc. Thesis Sharif University of Technology ; Faghihi Sani, Mohammad Ali (Supervisor)
Abstract
Gelcasting is a new ceramic forming technique getting worldwide attention. The process is based on casting of slurry; containing powder, water and water-soluble organic monomers. The premix solution was prepared using Acrylamide as a monomer and Methylene bisacrylamide as a crosslinker with AM:MBAM ratio of 25:1, and Poly Acrylic Acid Sodium as a dispersant (1 wt% based on ceramic powders weight). A series of Al2O3/ZrO2 ceramic nanocomposites with 15, 17.5 and 20 wt% content of ZrO2 and 40, 43, 45, 47, 50, 53 and 55 vol.% of solid loading were fabricated by gelcasting. After casting the mixture, the monomer was polymerized to form gel parts. Drying, burning out and sintering completed the...
Cataloging briefMechanical Properties of Al2O3-ZrO2 Nanocomposites Fabricated by Gelcasting, M.Sc. Thesis Sharif University of Technology ; Faghihi Sani, Mohammad Ali (Supervisor)
Abstract
Gelcasting is a new ceramic forming technique getting worldwide attention. The process is based on casting of slurry; containing powder, water and water-soluble organic monomers. The premix solution was prepared using Acrylamide as a monomer and Methylene bisacrylamide as a crosslinker with AM:MBAM ratio of 25:1, and Poly Acrylic Acid Sodium as a dispersant (1 wt% based on ceramic powders weight). A series of Al2O3/ZrO2 ceramic nanocomposites with 15, 17.5 and 20 wt% content of ZrO2 and 40, 43, 45, 47, 50, 53 and 55 vol.% of solid loading were fabricated by gelcasting. After casting the mixture, the monomer was polymerized to form gel parts. Drying, burning out and sintering completed the...
Find in contentBookmark |
|