Sharif Digital Repository

Usage of electroless Ni-B coatings as coatings with super hardness and wear resistance has been increased widely, but these coatings have low resistance to corrosion.In this project, in order to increase resistance to corrosion, titania powder of szie 200 to 300 nanometers is added to Ni-B coatings to make a composite coating of Ni-B-TiO2 that has better corrosion properties compared to Ni-B coatings. Ultrasonic use for creating composite coatings of Ni-B-TiO2 and the optimum ultrasonic and electroless bath conditions for creating optimum coating in terms of corrosion resistance are determined. These optimum conditions are as follows: speed of 300 rpm for substrate circulation in bath, 250 W... 

In this research, TiO2 nano-particles were electrophoretically deposited on the FTO glass to produce self-cleaning property. Two type of suspensions with different TiO2 nano-powders were used. Merck and fabricated by sol-gel route, TiO2 nano-powders were utilized in suspensions and Conductivity, pH and zeta potential of suspensions were determined. Electrophoretic deposition of two kind of suspensions was performed in different voltages of 10, 30 and 60V (for 10s) and room temperature. TiO2 coatings were sintered in 450oC for 1 hour. The phase transformation of TiO2 films were measured using XRD. Morphology, average particle size and thickness of TiO2 films were analyzed using FESEM... 

In this study, the photocatalytic activity and hydrophilicity of coat improved using Nitrogen and Vanadium elements as dopant in TiO2 coating. By using vanadium and nitrogen elements and silica prelayer, a titania coating was deposited on the soda-lime glass substrate by sol-gel dip coating method to produce self-cleaning surface. XRD and FTIR analyses were done on the powders after heat treating at in 450˚C for 30 min. XPS analysis was done for investigation of N replacement in titania structure. The band-gap energy of formed anatase was derived using UV-Vis analysis. The coating morphology and thickness were also investigated by SEM. Hydrophilicity of coatings was determined by measuring... 

Improving the photocatalytic activity of titania nanoparticles and Cognition the mechanisms governing this property, has received more attention in the recent few years. One of the main strategies for improving the photocatalytic activity and modifying the bandgap structure of titania nanoparticles, is incorporation different metallic and nonmetallic ions in the titania lattice. In this study, 1%Fe, 1%Gd and 2%P (molar ratio) doped titania nanoparticles were successfully prepared by a modified sol-gel method in room temperature. The products were characterized with various spectroscopic and analytical techniques to determine their structural, morphological, physicochemical and... 

In recent decade, photocatalystic properties of titania nanotube and its mechanisms has been considered greatly in many researches. One of the major ways to increase photocatalystic properties and extending the usage of TNTs is doping them with various elements and modifying their band structure. In present research doped TNTs were prepared by doping of Molybdenum, Nitrogen, and Carbon elements by anodizing method in about of 35 degrees of centigrade and constant voltage of 20V on the surface of titanium sheet. Structural and photocatalystic properties of as-prepared TNTs were studied using field emission scanning electron microscope (FESEM), x-ray diffraction (XRD), energy dispersive... 

Metallic implants are useful in dental and orthopedic applications. Bio coating is necessary to improve bio-compatibility and bio-activation of metallic implants. For this goal, HA is the most important material. In this research, the goal is to improve bio-compatibility of St. St 316 by coating HA, HA-ZrO2, HA-TiO2, HA-ZrO2-TiO2 using combination of electrodeposition and electrophoretic methods. To form HA, calcium and phosphor salt solution was used then ZrO2- TiO2 nanoparticles was added to solution. In order to analyst the coatings different tests were done. Thickness analysis, XRD, FT-IR, FE-SEM and EDS, bonding Strength, Polarization test, bio-compatibility and surface roughness... 

In this project, the nanostructured titanium oxide with heaily doping of oxides of cerium and tin was synthesized using the sol-gel process and its properties were studied. To synthesize TiO2, titanium tetraisopropoxide precursor was used. Cerium nitrate and aqueous tin chloride precursors were utilized for cerium and tin synthesis. Then, they were mixed with Titania precursor causing a severe doping. After that, a gel was produced and it was aged and eventually, it was dried and calcined. XRD and SEM were used to determine the phase and particle size SEM and XRD results showed that doping had great impact on TiO2 crystals. The approximate size of nanoparticles was calculated using... 

Ceramic coatings on metallic substrates are used in many different applications. In biomaterials science, hydroxyapatite coating due to its similarity to the mineral part of bone structure is used to modification of implants surface. In this research, the HA/TiO2 double layer was coated on Ti-6Al-4V by sol- gel dip-coating method. After preparation of stable TiO2 sol, the Ti-6Al-4V substrate was dipped into the TiO2 sol. The speed of dipping was 10cm/min. After drying at 80°C, the TiO2 layer heat-treated at different temperature (350-500°C) for 1h. The HA outer layer was coated by dipping of Ti-6Al-4V substrate with TiO2 layer into HA sol, followed by heat-treatment at different temperatures... 

In this study the effect of nanoparticles on the mass transfer of dispersed phase in the liquid-liquid extraction systems, containing toluene with acetic acid as dispersed phase and saturated water of toluene as continues phase was investigated. For the ease of dispersion of nanoparticles in nonpolar organic dispersed phase, with the use of a novel method, hydrophobic tiania nanoparticles were synthesized and during producing with the sole-gel method were modified by adding Tetraethyl Ortho titanate as modifying agent, also the smallest hydrophobic nanoparticles of magnetite were synthesized by co-precipitating method and then, under optimum thermal condition were coated by adding Oleic... 

Titania is semiconductor material and have many applications including photocatalysis, photochromic, air and water purification, sensors, and solar cell. In electrophoretic deposition, charged particles dispersed in a stable suspension move towards an oppositely charged electrode, and form dense layer of deposit on it. In this investigation electrophoretic deposition of titania nano-particles in suspensions prepared by different solvents (methanol, ethanol and butanol) with and without dispersant (triethanolamine and polyethylenimine), was studied. Well stabilized suspensions, prepared for electrophoretic deposition. The effects of solvent type, additive concentration, mechanism of particles...