Sharif Digital Repository

In this investigation a new type of superabsorbent hydrogel based on agar was prepared, and the effect of the feed ratio of some components (acrylic acid, MBA, APS and agar) on the swelling capacity of the hydrogel was systematically studied. Maximum water absorbency of the optimized final product was found to be 1,100∈g/g in distilled water. The structure of the hydrogel was characterized by FT-IR method and morphology of the samples was examined by scanning electron microscopy (SEM). Swelling properties of optimized hydrogel sample in different swelling mediums were investigated. The optimum hydrogel were also loaded with potassium nitrate and its potential for controlled release of... 

This article reports the first oil-absorbent cross-linked copolymer consisting of modified multiwalled carbon nanotube (MWCNT) and showing high oil absorbency. Also, to investigate and evaluate the effective parameters on oil absorbency, cross-linked dodecyl methacrylate (DDMA)-diphenylacrylamide (DPAA) and DDMA-butyl acrylate (BA) copolymers were synthesized. DDMA was copolymerized with different mol% of DPAA or BA and cross-linked using azobisisobutyronitrile as the initiator and various weight percentages of 1,4-butandiol dimethacrylate, methylene bisacrylamide, or vinyl group-modified MWCNT cross-linkers. The effects of monomer feed composition, cross-linker concentration, and the... 

Temperature-sensitive hydrogels based on N-t-butylacrylamide (TBA), acrylamide (AAm), and sodium alginate were prepared by free radical polymerization method. Methylenebisacrylamide (MBA) and amonium persulfate (APS) were applied as water soluble crosslinker and initiator, respectively. The chemical structure of the hydrogels was confirmed by FT-IR spectroscopy and thermogravimetric analysis (TCA) methods. Morphology of the samples was examined by scanning electron microscopy (SEM). By changing the initial TBA/AAm mole ratios, hydrogels with different swelling properties were obtained. The rate parameters were found to be 2.0, 2.4, and 3.5 min for the superabsorbents with AAm/TBA weight... 

Homopolymer hydrogel of 2-acrylamido-2-methylpropane sulfonic acid (AMPS) and its nanocomposite counterpart were prepared to study their swelling properties. The hydrogels showed ability to absorb and retain electrolytes as well as binary mixtures of water and organic solvents (i.e., methanol, ethanol, acetone, ethylene glycol (EG), polyethylene glycol, N-methyl-2-pyrrolidone (NMP), and dimethylsulfoxide (DMSO). The nanocomposite gel exhibited lower swelling in all solvent compositions in comparison with non-composite gel. Unlike conventional acrylic acid-based hydrogels, the poly(AMPS) gels showed superabsorbing capacity in pure ethanol, methanol, EG, DMSO and NMP. Meanwhile, swelling... 

A series of biopolymer-based superabsorbent hydrogels based on carboxymethyl cellulose has been prepared by free-radical graft copolymerization of acrylamide and 2-acrylamido-2-methylpropan sulfonic acid (AMPS) in aqueous solution using methylenebisacrylamide as a crosslinking agent and ammonium persulfate as an initiator. The effect of variables on the swelling capacity such as: acrylamide/AMPS weight ratio, reaction temperature, and concentration of the initiator and crosslinker were systematically optimized. The results indicated that with increasing the amount of AMPS, the swelling capacity is increased. FT-IR spectroscopy and scanning electron microscope analysis were used to confirm... 

Preformed particle gels (PPGs) in solutions have been widely used to suppress excess water production in mature oil reservoirs and, in turn, to improve the amount of oil recovery in brown oil fields. In this study, PPG solutions were meticulously formulated and synthesized in order to be utilized in harsh environments in terms of pressure, temperature, pH, and salinity from a free radical polymerization process. In this work, nanosilica gel at different weight percentages was added to improve the mechanical and thermal stability properties of the PPG at harsh condition: high pressure, temperature, and strain. Moreover, the effects of nanosilica gel at various concentrations, ranging from 0.0...