The effect of substrate temperature on epitaxial growth of Y1Ba2Cu3O7−x film deposited on (100) crystalline lanthanum aluminate (LAO) substrates by RF Sputtering method has been investigated. The crystal mismatch between film and substrate is about 1.6%. The sputtering was carried out in vacuum with base pressure better than 10−5 Torr and 10/20 Pa oxygen/argon partial pressures. Substrate temperature at this condition is about 730 °C based on Bormann–Hammond diagram. As well known, because of the small lattice mismatch between YBCO and LAO, fabricated thin films are not perfectly c-axis and there is tendency to form a/b-axis regions in the film. Due to substantial effects of the density and... 

A novel biopolymer-based hydrogel composite was synthesized through chemical crosslinking by graft copolymerization of partially neutralized acrylic acid onto the hydrolyzed collagen. The Taguchi method, a robust experimental design, was employed for the optimization of the synthesis based on the swelling capacity of the hydrogels. This method was applied for the experiments and standard L16 orthogonal array with five factors and four levels. In the synthesis of the composite superabsorbent, N,N′-methylene bisacrylamide (MBA) as crosslinker, ammonium persulfate (APS) as initiator, acrylic acid (AA) as monomer, neutralization percent (NU), and collagen/kaolin weight ratio were used as... 

According to previous studies on the fracture surface morphologies of bulk metallic glasses, the stable crack growth region width and vein pattern size increase with the plasticity at room temperature. In the present work, the fracture surface morphologies of Ti- and Zr-based bulk metallic glasses bent over a wide temperature range (0.1–0.8 glass transition temperature) are systematically analyzed. According to our finding, the stable crack growth region width increases while the vein pattern size decreases as the ductility improves by varying temperature. This observation is in contrast to the common thought that the ductility is proportional to the stable crack growth region width and vein... 

In this research, the influence of anionic surfactant sodium dodecyl sulfate (SDS), pH, substrate finishing, and annealing temperature on the surface morphology and hardness of the electroless nickel phosphorus (ENi-P) coatings were studied. Taguchi's experimental design method was used. Parameters selected in three levels and L9 from orthogonal robust array design were employed. Surface roughnesses of the deposits were measured using a stylus instrument. Scanning electron microscope and x-ray diffraction analysis were implemented to study surface morphologies and phase composition, respectively. Microhardness of the ENi-P deposits was measured using a microhardness tester at three trials... 

Zn/Ni nanocrystalline multilayer coatings were electrodeposited using single bath method and switching current densities. Effect of deposition current densities (i1 and i2) and number of layers (n) on composition, surface morphology and roughness, microhardness, phase structure and corrosion resistance of Zn/Ni multilayers were studied and compared with that of single layer. Analyzing and optimizing the influences of mentioned parameters on corrosion resistance of multilayers carried out through Response Surface Methodology. The model based on RSM results demonstrated that improvement in corrosion resistance due to increase in “difference of deposition current densities” was more effective... 

Indium tin oxide (ITO) thin films have been deposited using RF sputtering technique at different pressures, RF powers, and substrate temperatures. Variations in surface morphology, optical properties, and film resistances were measured and analyzed. It is shown that a very low value of sheet resistance (1.96 ω/sq.) can be achieved with suitable arrangement of the deposition experiments. First, at constant RF power, deposition at different pressure values is done, and the condition for achieving minimum sheet resistance (26.43 ω/sq.) is found. In the next step, different values of RF powers are tried, while keeping the pressure fixed on the previously found minimum point (1-2 Pa). Finally,... 

Nanoscratch testing is a highly reliable method used to extract a variety of film properties. It is proven that many of the experimental factors can influence the obtained results, such as the probe tilt, the scratch depth, etc. On the other hand, the surface roughness of the samples is an important parameter in nanoscratch and other similar tests, including the nanoindentation test. Thus, the effect of surface roughness on both the nanoscratch experiments and finite element simulations has been investigated. By performing scratch tests on gold and copper films and carrying out the finite element (FE) simulations on the rough and smooth surfaces, the importance of surface morphology was... 

Purpose: The morphological stability of silicon single crystal wafers was investigated, after performing cleaning surface treatments based on moderate temperature annealing and plasma sputtering. Methods: The wafer surfaces were measured by Tapping mode atomic force microscopy in air, before and after the different treatments. The 3D images were segmented by watershed algorithm identifying the local peaks, and the stereometric parameters were extracted thereof. The analysis of variance allowed to better assess the statistically significant differences. Results: All the resulting quantities were critically discussed. It appeared that the different cleaning treatments affected differently the... 

We have studied formation of Au-Ag alloy nanoparticles in sputtered SiO 2 thin films. Silica thin films containing Au-Ag nanoparticles were deposited on quartz substrates using rf reactive magnetron co-sputtering technique. The films heat-treated in reducing Ar + H 2 atmosphere at different temperatures. They were analyzed by using UV-vis spectrophotometry, atomic force microscopy and X-ray photoelectron spectroscopy (XPS) methods for their optical, surface morphological as well as structural and chemical properties. The optical absorption of the Au-Ag alloy nanoparticles illustrated one plasmon resonance absorption peak located at 450 nm between the absorption bands of pure Au and Ag... 

The influence of annealing temperature on the hydrophilic property of WO3 thin films deposited by thermal evaporation and sol-gel dip-coating methods was studied and compared for the first time. The thermal evaporated WO3 thin films annealed at 400 °C showed a nearly super-hydrophilic property without UV and visible illumination. By analysing the O(1s) core level peak of XPS spectra, the amount of oxygen contributed at various bonds (including O2-, OH- and H2O) on the surface of the annealed samples at different temperatures were measured. In addition, a correlation between the hydrophilicity and the concentration of chemisorbed water on the film surface was suggested, independent of the... 

The mixed nano-ferrites materials Cu0.6Zn0.4HoxFe2−xO4 (0.00 ≤ x ≤ 0.12) were prepared via the sol–gel auto combustion technique. The TGA curve established the annealing temperature (500 °C) for phase formation. The single exothermic peak on the DSC plot occurred at 341 °C temperature. XRD patterns of these nano ferrites verified single phase formation of the FCC cubic structure. The lattice constant a was increased from 8.4244 to 8.4419 Å and then its value decreased to 8.4319 Å. Crystallite size was found in the range of 7 to 16 nm. The surface morphology of the samples was observed from the scanning electron microscope (SEM) images. The grain size was found within the range of 90 nm to... 

The mixed nano-ferrites materials Cu0.6Zn0.4HoxFe2−xO4 (0.00 ≤ x ≤ 0.12) were prepared via the sol–gel auto combustion technique. The TGA curve established the annealing temperature (500 °C) for phase formation. The single exothermic peak on the DSC plot occurred at 341 °C temperature. XRD patterns of these nano ferrites verified single phase formation of the FCC cubic structure. The lattice constant a was increased from 8.4244 to 8.4419 Å and then its value decreased to 8.4319 Å. Crystallite size was found in the range of 7 to 16 nm. The surface morphology of the samples was observed from the scanning electron microscope (SEM) images. The grain size was found within the range of 90 nm to... 

Commercially pure titanium samples were exposed to grit blasting and acid-alkali treatments to obtain a variety of surface compositions and morphologies. Contact roughness test and microstructural studies were employed to study the surface topography of the samples. The nature and chemical composition of surface phases were evaluated using X-ray diffraction and microanalysis techniques. Selected samples first exposed to in vitro environment were then tested to determine the surface morphology and surface microstructure. Based on the data presented in this work, it is suggested that grit blasting process utilized prior to chemical treatment stage, yields a high quality surface morphology.... 

Since there have been many difficulties in clinical administration of anticancer drugs due to their poor solubility & targeting, development of new biodegradable Nano-carriers can provide good solutions to overcome the most of recent problems to obtain a better controlled release and targeted delivery of drugs with better efficiency and less side-effects. Acidic pH is regarded as a phenotypic characteristic of cancer tumors. Under this acidic condition, it is known that the surface charge of Chitosan-modified nano-particles become more positive. On the other hand, cancer cells are negatively charged. It is worth mentioning that by loading of anticancer drugs into this novel system, a strong... 

Various morphologies of CuO/Cu(OH)2 nanostructures with different adsorbed -OH contents were synthesized on an acid-treated Cu foil through variation of NaOH concentration from 0 to 50 mM with an in situ oxidation method. X-ray diffractometry and X-ray photoelectron spectroscopy (XPS) indicated formation of CuO on the Cu(OH)2 crystalline phase at a growth temperature of 60°C for 20 h. Antibacterial activity of the nanostructures against Escherichia coli bacteria was studied in the dark and under light irradiation. The nanostructures grown at a NaOH concentration of 30 mM showed the highest surface area and the strongest antibacterial activity among the samples. After elimination of the... 

V2O5-TiO2 nanostructured porous layers were grown through micro arc oxidation of titanium in vanadate containing electrolytes. This study sheds light on the effect of the electric current type on the photocatalytic performance of the layers. Surface morphology of the layers was investigated by SEM. The results revealed a porous structure with a pores size of 30-180 nm depending on the frequency and the duty cycle. A uniform porous structure was obtained under the pulse-DC regime. Topographical investigations revealed a rough surface which is favorable for catalytic applications. Our XRD and XPS results showed that the layers consisted of anatase, rutile, and vanadium oxide phases whose... 

Thin films of (WO3)1-x-(Fe2O 3)x composition were deposited by thermal evaporation on glass substrates and then all samples were annealed at 200-500 °C in air. Optical properties such as transmittance, reflectance, optical bangap energy, and the optical constants of the "as deposited" and the annealed films were studied using ultraviolet-visible spectrophotometry. It was shown that the annealing process changes the film optical properties which were related to Fe2O3 concentration. Moreover, using X-ray photoelectron spectroscopy, we have indicated that WO3 is stoichiometric, while iron oxide was in both FeO and Fe2O3 compositions so that the FeO composition converted to Fe2O3 after the... 

In this study a hot filament chemical vapour deposition (HFCVD) technique was used to prepare Fe-Cr films on Si substrate as catalysts for thermal CVD (TCVD) growing of carbon nanotubes (CNTs) from liquid petroleum gas (LPG) at 800 °C. To characterize the catalysts or CNTs, X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Raman spectroscopy were used. The XPS spectra obtained at different stages of Ar+ sputtering revealed that in the depth of catalyst layers, the relative Fe-Cr concentrations are higher than the top-surface. SEM images of samples after TCVD indicate a significant CNT growing at the backside of catalyst...