Sharif Digital Repository

A hydrophilic macromolecular network is prepared by performing graft opolymerization of poly (sodium acrylate) chains onto salep and silica gel. The reaction parameters affecting the water absorbency of the superabsorbent composite were optimized using Taguchi method. FT-IR spectroscopy and Thermo Gravimetric Analysis (TGA) were used for confirming the structure of the final product and morphology of the synthesized superabsorbent composite was examined by SEM. The swelling behavior of optimum superabsorbent composite was measured in various swelling media. In addition, swelling kinetics and on-off switching behavior were investigated. In order to evaluate the controlled release potential of... 

A novel superabsorbent hydrogel composite based on gelatin has been prepared by graft copolymerisation of acrylic acid and acrylamide in the presence of kaolin powder, using methylene-bisacrylamide (MBA) as a crosslinking agent and ammonium persulfate as an initiator. The synthetic variables affecting the water absorbency of the resulting superabsorbent composite were studied and the composite structure was confirmed using FT-IR spectroscopy. A new absorption band at 1728 cm-1 in the composite spectrum confirmed the presence of a kaolin-organic polymer linkage. The effect of kaolin content and MBA concentration showed that increasing these parameters decreased the water absorbency of the... 

A novel superabsorbent composite based on sodium alginate and the inorganic clay kaolin was synthesized via the graft copolymerization of acrylic acid (AA) in an aqueous medium with methylene bisacrylamide (MBA) as a crosslinking agent and ammonium persulfate (APS) as an initiator. The effects of reaction variables, such as the MBA, AA, and APS concentrations and the alginate/kaolin weight ratio, on the water absorbency of the composite were systematically optimized. Evidence of grafting and kaolin interactions was obtained by a comparison of the Fourier transform infrared spectra of the initial substrates with that of the superabsorbent composite, and the hydrogel structure was confirmed... 

A novel superabsorbent hydrogel composite based on kappa-carrageenan (κC) was prepared by graft copolymerisation of acrylic acid (AA) in the presence of kaolin using methylenebisacrylamide (MBA) as a crosslinking agent and ammonium persulfate (APS) as an initiator. The synthetic variables (i.e. AA, MBA and APS concentration, and the amount of kaolin) affecting the water absorbency of the resulting superabsorbent composite were studied. Evidence of grafting and kaolin interaction was obtained by comparing the FTIR spectra of the initial substrates and of the superabsorbent composite. A new absorption band at 1722 cm-1 in the composite spectrum confirmed the kaolin-organic polymer linkage.... 

In the present study, we attempt to synthesize and characterize novel CMC-g-poly (acrylic acid-co-2-acrylamido-2-methylpropanesulfonic acid)/silica gel composite. Infrared spectroscopy and TGA thermal analysis were carried out to confirm the chemical structure of the hydrogel. Moreover, morphology of the samples was examined by scanning electron microscopy. The effect of reaction variables affecting on water absorbency of the composite and swelling behavior in various solvents, salt, and pH solutions was investigated. Maximum water absorbency of the optimized final product was found to be 4000 g/g in distilled water. The absorbency under load (AUL) of the hydrogel was also determined by... 

A novel kind of a biopolymer-based superabsorbent composite, salep-g-poly(sodium acrylate)/alumina, was prepared from salep, sodium acrylate, and alumina by aqueous polymerization, using N,N'-methylenebisacrylamide (MBA) as a cross-linker and ammonium persulfate (APS) as an initiator. The reaction parameters [i.e., acrylic acid (AA), MBA, APS amounts, and neutralization percentage of AA as well as alumina/salep weight ratio] affecting the water absorbency of the hydrogel composite were optimized using systematic method to achieve a composite with high swelling capacity as possible. The swelling behavior of optimum superabsorbent composite was measured in various pH solutions. In addition,... 

A series of superabsorbent composites were synthesized through graft copolymerization of acrylic acid (AA) onto carboxymethyl cellulose (CMC) in the presence of celite powder using N,N'-methylenebisacrylamide (MBA) as a cross-linking agent and ammonium persulphate (APS) as an initiator. The chemical structure and thermal properties of the composite hydrogels were characterized by FTIR spectroscopy and TGA methods, respectively. Morphology of the samples was examined by scanning electron microscopy (SEM). In free-state, the swelling conditions and hence the related data are not real, because in all their applications the swelling particles of superabsorbent must absorb aqueous solutions while...