Sharif Digital Repository

Assessment of mechanical properties of glass/metal joints is a challenging process, especially when the application relevant conditions of the joints have to be considered in the test design. In this study, a finite element method (FEM) is implemented to analyze a torsional shear strength test designed for glass-ceramic/steel joints aiming towards solid oxide fuel/electrolysis cells application. Deviations from axial symmetry of the square flanges (ends) of respective hourglass-shaped specimens and also supporting and loading sockets of the test set-up are included in the model to simulate conditions close to reality. Undesirable tensile stress and also shear stress concentration appear at... 

The structural integrity of the sealant is critical for the reliability of solid oxide cells (SOCs) stacks. In this study, elastic modulus (E), hardness (H) and fracture toughness (KIC) of a rapid crystallizing glass of BaO–CaO–SiO2 system termed “sealant G” are reported as determined using an indentation test method at room temperature. A wide range of indentation loads (1 mN–10 N) was used to investigate the load-dependency of these mechanical properties. Values of 95 ± 12 GPa, 5.8 ± 0.2 GPa and 1.15 ± 0.07 MPa m0.5 were derived for E, H and KIC using the most suitable indentation loads. An application relevant annealing treatment of 500 h at 800 °C does not lead to a significant change of... 

Interactions between the metal interconnect and glass sealant in the solid oxide cells stack are critical to retaining the system integrity. To address this issue, in the current study, 8YSZ coating is applied on the Crofer22 APU steel via sol-gel and dip-coating method. Dense and continuous 8YSZ coatings are obtained on Crofer22 APU substrates. X-ray diffraction and Raman spectroscopy results show that both cubic and tetragonal structures of 8YSZ are formed. A glass-based sealing paste is applied on bare and 8YSZ coated Crofer22 APU steel. The interfacial compatibility and chemical stability of steel/glass and steel/8YSZ/glass joint couples are investigated using SEM and EDS line scan... 

The structural integrity of the sealant material is critical for the reliability of solid oxide fuel/electrolysis stacks. In the current study, a torsion test is implemented to evaluate and compare its shear strength with a partially crystallized glass sealant at room- and operation relevant high-temperatures. Hourglass-shaped specimens with different configurations of hollow- and full-halves are utilized for testing. The fracture surfaces are visualized via optical microscopy and complementary scanning electron microscopy. In addition, cyclic loading is used to investigate potential subcritical crack growth effects in the sealants. Both, the specimens with a hollow-half as well as the ones... 

The conventional relations for calculating the fracture stresses consider only elastic deformation but ignore viscoelastic and viscoplastic behaviors. Measuring the joining strength of a composite glass sealant-metallic interconnect specimen at solid oxide cell application relevant at high temperatures is a case where such effects can become significant. In the current study, three-point and four-point bending test results were analyzed using the finite element method (FEM) to assess systematic and random errors. It is shown that plastic deformation of the steel interconnect material at high temperature, although having a large effect on the stress distribution in the... 

The structural integrity of the sealant is critical for the reliability of solid oxide cells (SOCs) stacks. In this study, elastic modulus (E), hardness (H) and fracture toughness (KIC) of a rapid crystallizing glass of BaO–CaO–SiO2 system termed “sealant G” are reported as determined using an indentation test method at room temperature. A wide range of indentation loads (1 mN–10 N) was used to investigate the load-dependency of these mechanical properties. Values of 95 ± 12 GPa, 5.8 ± 0.2 GPa and 1.15 ± 0.07 MPa m0.5 were derived for E, H and KIC using the most suitable indentation loads. An application relevant annealing treatment of 500 h at 800 °C does not lead to a significant change of...