Sharif Digital Repository

In this research, an attempt was made to improve TiO2 photo-catalyst properties, thus pure, N-Ce co-doped TiO2 thin films were prepared on glass-ceramic substrate using a sol-gel dip-coating technique. The samples were calcinated in air at 475 °C, 550°C, and 650°C for 2 h. The result of simultaneous thermal analysis (STA) and X-ray diffraction (XRD) showed that the presence of Ce in TiO2 could inhibit the phase transformation from anatase to rutile and enhance the thermal stability, and anatase was the dominant phase in N-Ce co-doped TiO2 samples. Also based on the results, the doping results in decreasing the size of TiO 2 crystallite. The results of ultra violet-visible light diffuse... 

Recently, nanodiamonds have attracted interest in biomedical applications such as drug delivery, targeted cancer therapies, fabrication of tissue scaffolds, and biosensors. We incorporated diamond nanoparticles in alginate-bioactive glass films by electrophoretic process to prepare functional coatings for biomedical implants. Turbidity examination by time-resolved laser transmittance measurement revealed that a stable multi-component aqueous suspension of alginate, bioactive glass and diamond particles could be obtained at concentrations of 0.6, 1.3, and 0.65 g/l, respectively. Uniform films with ~ 5 μm thickness were deposited on 316 stainless steel foils by employing constant field... 

SiO2-CaO-MgO glass and glass-ceramic powder doped with Nd 3+ were synthesized with sol-gel method. Tetraethylorthosilicate (TEOS), Ca(NO3)2·4H2O, Mg(NO 3)2·6H2O, Nd(NO3) 3·6H2O, ethanol, distilled water, and HNO 3 were used as starting materials. The synthesized powder's properties were examined with simultaneous thermal analysis (STA), X-ray diffraction (XRD), photoluminescence (PL) and scanning electron microscopy (SEM) analysis. The STA curves showed that the softening point and crystallization temperatures were shifted to higher temperatures with increasing dopant content. Regarding XRD patterns of glass samples, Nd was found to act as an intermediate oxide in glass matrix. The XRD... 

Pb(Zr 0.52Ti 0.48)O 3 (PZT) nanotubes with diameters of 80-100 nm and a wall thickness of 15-20 nm were prepared by sol-gel template technique and using multi-walled carbon nanotubes (MWCNT) as sacrificial templates. The coating process of MWCNT with PZT precursor sol and removal of the carbon nanotubes by an interrupt heat treatment were discussed and studied by Raman spectroscopy. Simultaneous thermal analysis (STA) revealed that PZT nanotube crystallized at the low temperature of 410°C by the significantly low activation energy of crystallization of 103.7 kJ/mol. Moreover, based on the X-ray diffraction (XRD) pattern and selected area electron diffraction pattern the crystal structure of... 

This work presents the catalytic graphitization process of phenolic resins (PR's) by addition of in situ nano-Fe particles as catalyst. Pyrolysis treatments of prepared compositions including various contents of nano-Fe particles were carried out at 600–1200 °C for 3 h under reducing atmosphere and graphitization process were evaluated by different techniques such as X-Ray diffraction (XRD), Field Emission Scanning Electron Microscopy (FESEM), High Resolution Transmission Electron Microscopy (HRTEM), Simultaneous Thermal Analysis (STA) and Raman spectroscopy that mainly performed to identify the phase and microstructural analysis, oxidation resistance and extend of graphitized carbon... 

Al–5·6Zn, Al–5·6Zn–2·5Mg and Al–5·6Zn–2·5Mg–1·6Cu (wt-%) powder blends were compacted at 350 MPa and sintered in nitrogen at different temperatures to study microstructural evolution during sintering. Densification, dimensional changes and mechanical properties of the Al alloys were investigated. Microstructural analyses were performed by scanning electron microscopy (SEM) coupled with energy dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), and simultaneous thermal analysis (STA) in order to determine the temperature and chemical composition of the phases formed during sintering. It was shown that various liquids and intermetallic phases including Al0·71Zn0·29 at 438°C,... 

Despite brilliant properties of glass ionomer cement (GIC), its weak mechanical property poses an obstacle for its use in medical applications. The present research aims to formulate hydroxyapatite/yttria-stabilized zirconia (HA/YSZ) in the composition of GIC to enhance mechanical properties and to improve fluoride release of GIC. HA/YSZ was synthesized via a sol-gel method and characterized by applying X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), X-ray photo-emission spectroscopy (XPS) and simultaneous thermal analysis (STA) along with transmission electron microscopy (TEM) methods. The synthesized nanocomposite was mixed with GIC at a fixed composition of 5.... 

A template-directed synthetic method, using surfactant cetyltrimethylammonium bromide (CTAB) as a template and co-surfactant polyethylene glycol (PEG600) as a co-template under hydrothermal conditions, has been applied to obtain dandelion-like HAp. The morphology, size, crystalline phase, chemical composition, physical characteristics, and thermal behavior of the product were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray powder diffraction (XRD), Fourier ransform infrared spectroscopy (FTIR), induced coupled plasma spectroscopy (ICP), BET (Brunauer, Emmett, and Teller) method, and simultaneous thermal analysis (STA). SEM and TEM...