Sharif Digital Repository

In this work, the effect of zircon content on the mechanical and chemical behaviors of injection molded silica-based ceramic cores has been investigated. In order to simulate a casting process condition, the sintered samples at 1220 C were consequently heated up to 1430 C. Three point bending tests were carried out on all the prepared samples. The chemical resistance of the prepared cores was evaluated by leaching of samples in 43% KOH solution at its boiling point. Phase evolution and microstructure were investigated by XRD and SEM, respectively. Results showed that increasing zircon content led to an increase in MOR and decrease in leachability owing to the decrease in content of fused... 

In this work, cristobalite crystallization and its effects on mechanical and chemical behaviour of injection moulded silica-based ceramic cores were investigated. In order to simulate casting process condition, the sintered samples at 1220 °C were also heated up to 1430 °C. Flexural strength test was carried out on both sintered and heat treated samples. Chemical resistance of the cores was evaluated by leaching the samples inside 43. wt% KOH solution at its boiling point. Phase evolution and microstructure were investigated by thermal analyses (DTA and DSC), X-ray diffraction (XRD), scanning electron microscopy (SEM) and optical microscopy (OM). Results showed that cristobalite was...