Sharif Digital Repository

This paper focuses on the determination of the complete set of ideal orientations of FCC materials in the equibiaxial tension mode of deformation. The simulations are based on the numerical procedure developed by the authors in which, a rate-sensitive crystal plasticity model with Secant hardening law was employed. The resulting nonlinear system of equations is solved by the modified Newton-Raphson method. An Euler space scanning method is used to obtain the ideal orientations of a deformation mode. In this method some initial orientations which are evenly spaced in the Euler space are selected and their evolutions into the ideal orientations are tracked. To verify the accuracy of the... 

Optimized conditions of hot and cold rolling followed by annealing can result in a balance between recrystallization and rolling textures in order to reduce the planar anisotropy of brass sheets. In this work, the effect of finish rolling temperature, cold reduction and annealing temperature on texture development has been investigated. It is shown that uniform deformation at higher finishing temperature is responsible of formation of a severe Cube and G texture components. In contrast, mechanical twinnings are widely formed at low finishing temperatures. There is also a direct relation between the intensity of Cube component and the amount of cold reduction  

The control of texture and microstructure can be achieved by an appropriate thermomechanical treatment in industrial production. The effects of finish rolling temperature, cold reduction and annealing temperature on texture development and microstructure in Brass sheet were investigated. The role of deformation inhomogeneities on texture evolution has been considered. The formation of transition bands during hot rolling enforced the intensity of cube components. Shear bands increased the intensities of S and Cu components after cold rolling and at higher cold reductions. Transition from Cu to Y and Y to Bs was completed better because of mechanical twinning. Thermal twins annihilated the... 

High strength TRIP-aided steel sheets with high formability and better ductility are of industrial interest. Texture control and retained austenite characterization are considered as the main factors with respect to the formability and ductility. In this work, the effect of cold rolling and intercritical annealing on texture development has been investigated for two TRTP-aided steel sheets, which are different in Si and Al content. Experiments show that the cold rolling extends the a and γ-fibers on these grades of steel. Intercretically annealing decreases the intensity of α-fiber and leads to sharpness of γ-fiber, especially for Al steel  

The effect of temper rolling and subsequent annealing on texture development and magnetic properties of semi-processed non grain oriented electrical steel has been investigated. The result shows that 5 % temper rolling and final annealing at 850 8C resulted in strong a-fiber component. The etch-pit technique shows that strain induced boundary migration is responsible for new texture component augmentation. Vibrating sample magnetometery reveals that maximum and minimum magnetic permeability are related to rolling and transverse directions, respectively. Average magnetic permeability is improved to some extent as a result of temper rolling and subsequent annealing. © Carl Hanser Verlag GmbH &... 

An interstitial free (IF) steel was severely deformed using accumulative roll bonding (ARB) process and warm rolling. The maximum equivalent strains for ARB and warm rolling were 4.8 and 4.0, respectively. The microstructure and micro-texture were studied using optical microscopy and scanning electron microscopy equipped with electron back scattered diffraction (EBSD). The grain size and misorientation obtained by both methods are in the same range. The microstructure in the ARB samples after 6 cycles is homogeneous, although a grain size gradient is observed at the layers close to the surface. The through thickness texture gradient in the ARB samples is different from the warm rolled...