In this work, Fe-Pd alloy films have been electrodeposited on different substrates using an electrolyte containing [Pd(NH3)4]2+ (0.02 M) and [Fe-Citrate]2+ (0.2 M). The influences of substrate and overpotential on chemical composition, nucleation and growth kinetics as well as the electrodeposited films morphology have been investigated using energy dis-persive X-ray spectroscopy (EDS), current-time transients, scanning electron microscopy (SEM), atomic force microscopy (AFM) and X-ray diffraction (XRD) patterns. In all substrates – brass, copper and sputtered fluorine doped tin oxide on glass (FTO/glass) – Fe content of the electrodeposited alloys increases by increasing the overpotential.... 

Copper-palladium alloys of different compositions are electrodeposited on nickel from aqueous solutions. These alloys are characterized by scanning electron microscopy (SEM) and energy dispersive X-ray analysis (EDX). The catalytic activity of these alloys toward oxygen reduction reaction (ORR) in alkaline solution is investigated using rotating disk electrode (RDE). The number of electrons transferred per O2 molecule (n) obtained at different potentials is close to 2 at low overpotential indicating HO2- formation and gradually increases to 4 at higher overpotentials indicating full reduction to OH-. It is shown that Cu-Pd alloys are better electrocatalysts than Pd with Pd-Cu-1 having 24.5%... 

In the present study, the electrodeposition of Fe, Pd and Fe-Pd alloys, in alkaline solutions, has been investigated. Using ammonium hydroxide and trisodium citrate as the complexing agents, it has been shown that the co-deposition of Fe and Pd is achieved due to diminishing the difference between the reduction potentials of these two metals. Cyclic voltammetry results clearly show that the electrodeposition processes are diffusion-controlled and the diffusion coefficients of Fe2+ and Pd2+ are 1.11 × 10-6 and 2.19 × 10-5 cm2 s -1, respectively. The step potential experiments reveal that nucleation mechanism is instantaneous with a typical three-dimensional (3D) growth. At low overpotentials,...