Sharif Digital Repository

Electro-oxidation of alcohols (methanol, ethanol, 1-propanol and 2-propanol) on nickel dispersed into a thick layer of poly-o-aminophenol on graphite electrode (GE/POAP-SDS/Ni) was investigated. Ni-doping into the polymeric film was achieved chemically followed by enrichment of Ni(III) through cycling the potential. The electro-oxidation of alcohols on GE/POAP-SDS/Ni were found to be dominated by direct electro-oxidation with some contribution from Ni(II)/Ni(III) couple. Rate constants for the electro-oxidation of methanol, ethanol, 1-propanol and 2-propanol as derived by chronoamperometry were 1.65 × 105, 1.31 × 105, 2.53 × 104 and 1.40 × 104 cm3 mol-1 s-1, respectively. Impedance... 

The electrocatalytic oxidation of methanol was studied over Ni, Co and Cu binary or ternary alloys on graphite electrodes in a NaOH solution (0.1 mol/L). The catalysts were prepared by cycling the graphite electrode in solutions containing Ni, Cu and Co ions at cathodic potentials. The synergistic effects and catalytic activity of the modified electrodes were investigated by cyclic voltammetry (CV), chronoamperometry (CA) and electrochemical impedance spectroscopy (EIS). It was found that, in the presence of methanol, the modified Ni-based ternary alloy electrode (G/NiCuCo) exhibited a significantly higher response for methanol oxidation compared to the other samples. The anodic peak... 

Nickel modified graphite electrodes (G/Ni) prepared by galvanostatic deposition were examined for their redox process and electrocatalytic activities towards the oxidation of methanol, ethanol, 1-propanol and 2-propanol in alkaline solutions. The methods of cyclic voltammetry (CV), chronoamperometry (CA) and impedance spectroscopy (EIS) were employed. In CV studies, the electrochemical response, peak current varied in the order of MeOH > EtOH > 1-PrOH > 2-PrOH. Under the CA regime, a higher catalytic rate constant obtained for methanol oxidation was in agreement with CV measurements. Lower charge transfer resistance was obtained for low carbon alcohols oxidation and significantly higher... 

Nickel and nickel-manganese alloy modified graphite electrodes (G/Ni and G/NiMn) prepared by galvanostatic deposition were examined for their redox process and electrocatalytic activities towards the oxidation of methanol in alkaline solutions. The methods of cyclic voltammetery (CV), chronoamperometry (CA) and impedance spectroscopy (EIS) were employed. In CV studies, in the presence of methanol NiMn alloy modified electrode shows a significantly higher response for methanol oxidation. The peak current of the oxidation of nickel hydroxide increase is followed by a decrease in the corresponding cathodic current in presence of methanol. The anodic peak currents show linear dependency upon the... 

Effect of cathodic enzymatic decolorization of reactive blue 221 (RB221) on the performance of a dual-chamber microbial fuel cell (MFC) was investigated. Immobilized laccase on the surface of a modified graphite electrode was used in the cathode compartment in order to decolorize the azo dye and enhance the oxygen reduction reaction. First, methylene blue which is an electroactive polymer was electropolymerized on the surface of a graphite bar to prepare the modified electrode. Utilization of the modified electrode with no enzyme in the MFC increased the power density up to 57% due to the reduction of internal resistance from 1000 to 750 Ω. Using the electropolymerized-enzymatic cathode...