Corrosion of lead silicate glass (LSG) contacting 0.5 M aqueous nitric acid (HNO 3) was investigated via scanning electron microscopy, energy-dispersive spectroscopy, inductively coupled plasma analysis, and weight-loss measurement to determine the respective contributions of the ion-exchange vs. the hydrolysis reactions. The LSG having X M ≡ Pb+K+Na/Si mole ratios of less than 0.7 showed very little weight loss with no Si network deterioration. At X M > 0.7, the mechanism changed into the hydrolysis, which caused the formation of a networkless gel layer resting at the solid/liquid interface. Addition of titania (TiO 2) and zirconia (ZrO 2) had disparate effects: X M < 0.7 improved corrosion... 

Crystalline anatase TiO2 nanoparticles were synthesized in the gas phase using an H2O-assisted atmospheric-pressure CVS process. Simultaneous oxidation/hydrolysis of TiCl4 in the H2O-assisted APCVS process demonstrates the feasibility of facile fabrication and the designed synthesis of TiO2 nanoparticles in atmospheric pressure. Kinetics and thermodynamics studies of TiCl4 reactions in the gas phase illustrated oxidation or hydrolysis domination theoretically and were confirmed by experimental runs. Effects of H2O/O2 ratio on the reactions mechanisms, phase formation, size characteristics, morphology, and purity of TiO2 nanoparticles were experimentally studied using various analytical... 

Hydrolysis kinetics of the lead silicate glass (LSG) with 40 mol% PbO in 0.5 N HNO3 aqueous acid solution was investigated. The surface morphology and the gel layer thickness were studied by scanning electron microscopy (SEM) micrographs. Energy dispersive X-ray spectroscopy (EDS) and inductively coupled plasma spectroscopy (ICP) were used to determine the composition of the gel layer and the aqueous solution, respectively. The silicon content of the dissolution products was determined by using weight-loss data and compositions of the gel layer and the solution. The kinetic parameters were determined using the shrinking-core-model (SCM) for rate controlling step. The activation energy...