Formation of transparent glass-ceramic in the system MgO-SiO 2-Al 2O 3-K 2O-B 2O 3-F with and without addition of LiF and NaF has been investigated. Crystallization of glass-sample was conducted by controlled thermal heat-treatment, at determined nucleation and crystallization temperatures. In this regard, the effects of addition of LiF and NaF were investigated on the crystallization behavior and transparency of the samples. Low transmission (less than 80% at 600. nm) was observed in the basic composition (K).The addition of NaF and LiF caused more intense phase separation in the system. The results indicated that the glass-ceramic can remain transparent if fine grains with nano size are... 

SiO2-CaO-MgO glass and glass-ceramic powder doped with Nd 3+ were synthesized with sol-gel method. Tetraethylorthosilicate (TEOS), Ca(NO3)2·4H2O, Mg(NO 3)2·6H2O, Nd(NO3) 3·6H2O, ethanol, distilled water, and HNO 3 were used as starting materials. The synthesized powder's properties were examined with simultaneous thermal analysis (STA), X-ray diffraction (XRD), photoluminescence (PL) and scanning electron microscopy (SEM) analysis. The STA curves showed that the softening point and crystallization temperatures were shifted to higher temperatures with increasing dopant content. Regarding XRD patterns of glass samples, Nd was found to act as an intermediate oxide in glass matrix. The XRD... 

In this study, Li2O-TiO2-P2O5-x(Fe2O3) (x = 0, 2.5, 5 and 7.5 weight part) glass and glass-ceramics were synthesized through conventional melt-quenching method and subsequently heat treatment. Glass samples were studied by UV–visible spectroscopy and crystallized samples were characterized by differential thermal analysis, X-ray diffractometry and field emission scanning electron microscopy. Besides, electrical properties were examined according to the electrochemical impedance spectroscopy techniques. Experimental optical spectra of the Fe2O3-doped glasses revealed strong UV absorption band in the range of 330–370 nm, which were attributed to the presence of Fe3+ ions. The major crystalline... 

In the bone tissue engineering field (BTE), it is of significant importance to develop bioactive multifunctional scaffolds with enhanced osteoconductivity, osteoinductivity, and antibacterial properties required for lost bone tissue regeneration. In this work, a bioactive glass-ceramic scaffold was manufactured via a novel polymer-derived ceramics (PDC) manufacturing method. To gain antibacterial properties, the silver ions were incorporated in controlled amount along with other precursors in the PDC processing stage. Microstructural and structural properties of the fabricated silicate-phosphate glass-ceramic scaffold were evaluated by scanning electron microscopy (SEM) equipped with energy...