In this study, titanium dioxide (TiO2) nanotube array (TNA) films are fabricated via anodization of titanium (Ti) sheet. After annealing, the films consisted of well ordered, vertically oriented TNAs of 125±6nm diameter, 38±3nm wall thickness, and 2.9±0.3μm in length. Cadmium sulfide (CdS) nanoparticles are deposited on the synthesized TNAs by sequential-chemical bath deposition (S-CBD) method with different immersion cycle (n) to produce heterogeneous TNA/CdS-n (n=10, 20 and 30) nanostructures. UV-visible absorption spectra of the samples revealed that the absorption edge of CdS modified TNAs was shifted to a higher wavelength with respect to the pure TNAs indicating band gap reduction of... 

CdS nanoparticles were grown using CdSO4 and Na 2S2O3 as the precursors and thioglycerol (TG) as the capping agent. TG was shown to exhibit a catalytic role in the reaction and also acted as a capping agent. It was demonstrated that size growth is linearly related to the temperature of the reaction, i.e.the sizes can be controllably adjusted by temperature. The crystalline phase of the nanocrystals was also dependent on the temperature of growth: higher temperature favours the cubic phase. The pH also plays an important role in nanoparticle growth, as lower pH leads to a higher release rate of sulfur species. At pH as high as 10, the growth rate remains slow even at boiling temperature. This... 

In this work we report fabrication of a nanocrystal (NC)-based hybrid organicinorganic LED with structure of ITO/PEDOT:PSS/PVK/CdS-NCs/(Al or Mg:Ag). The hydrophilic CdS NCs were synthesized using a novel aqueous thermochemical method at 80 °C and sizes (around 2 nm) were controlled by thioglycolic acid (TGA) as the capping agent. The favorite feature of these NCs is their relatively high emission intensity and broad, near-white emission. The hydrophilic CdS NCs were successfully spin coated using Triton X-100 as the wetting agent. The fabricated LEDs demonstrated a turn on voltage about 7 V for Al metallic contact. The electroluminescence was a broad spectrum at 540 and 170 nm width, which... 

In this work, we propose a combined photochemical-chemical method that enables us to grow CdS nanoparticles with ångström precision. CdS nanoparticles were formed through a photo-induced reaction between CdSO 4 and Na2S2O3. Thioglycerol (C 3H8O2S) was used as the capping agent. Fine tuning of the size was subsequently carried out by controlling the pH of the solution. Optical absorption spectroscopy was mainly used to monitor the process of particle formation, and to measure the bandgap and size. X-ray diffraction spectra confirmed the optical sizes and demonstrated crystalline nanoparticles. In the presence of the capping agent there was a dark growth that was completely dependent on the pH... 

We studied the effect of target annealing temperature on optical and structural properties and composition of CdS thin films prepared by pulsed Nd:YAG laser. Deposited samples from annealed targets at 300 °C showed a mixed cubic and hexagonal structure, a band gap of about 2.56 eV and Cd/S ratio equal 1. This ratio increased to 2.40 and its band gap decreased to 2.46 eV when the sample was annealed at 500 °C for 1 h in air. However, films prepared from annealed targets at 500 °C became dark due to existence of polymorphous phase of CdO. Films changed to transparent yellow color with a hexagonal CdS structure and some peaks related to CdO after annealing above 250 °C in air. Its band gap... 

A photochemical approach on the size control of CdS nanoparticles is presented. CdS nanoparticles were grown using the photo-induced reaction of sodium thiosulfate with Cadmium sulfate, in the absence of any surfactant. Particles of 5.5-11 nm were obtained by changing the illumination time. The dark growth of nanoparticles was negligible, however we found by optical scattering measurements that a ripening phenomenon occurs and the size of nanoparticles slightly increases with time. © 2005 Elsevier B.V. All rights reserved  

In the present work a new strategy for straightforward fabrication of CdS/CdTe solar cells, containing CdS nanowires and nanoparticles as a window layer and CdTe nanoparticles and microparticles as an absorber layer, are reported. CdS and CdTe nanostructures were synthesized by solvothermal method. X-ray diffraction analysis revealed that highly pure and crystallized CdS nanowires and nanoparticles with hexagonal structure and CdTe nanoparticles with cubic structure were obtained. Atomic force microscope and field emission scanning electron microscope images showed that CdS nanowires with length of several μm and average diameter of 35 nm, CdS nanoparticles with average particle size of 32... 

The efficiency of planar perovskite solar cells (PSCs) with SnO2 as electron transport layer is already more than 19% achieved under controlled atmosphere. PSCs with solution processed SnO2 show high hysteresis and low fill factor. One way to improve the planar PSCs is using buffer layer between electron transport layer and perovskite to enhance the photo-electron extraction process. In this study, SnO2 and SnO2/CdS layers were fabricated by solution process using a suspension including CdS nanoparticles synthesized via a simple solution route. Then planar PSCs with the structure of Glass/FTO/ETL/Perovskite/Sprio-OMeTAD/Au were fabricated in ambient air condition using SnO2 and SnO2/CdS as... 

CdS nanocrystals were thermochemically (thermally activated) synthesized thorough the reaction between CdSO4 and Na2S 2O3 in an aqueous solution. Thioglycolic Acid (TGA) was used as the capping agent and catalyst of the reaction. The method was based on heat activated dissociation of Na2S2O3 and controllable release of S and free electrons in the solution. CdS NCs were formed by heating the sample solution at 96 C for 1 h. The results of optical spectroscopy and transmission electron microscopy demonstrated round shape NCs with sizes about 3.0 nm. The nanocrystals were also luminescent and represented a broad emission with a peak located at 515 nm and FWHM of 160 nm. Several samples were... 

Vertically aligned ZnO@CdS nanorod heterostructure films with various loadings of CdS nanoparticle shell were synthesized and applied in photoinactivation of Escherichia coli bacteria under visible light irradiation. While neither the bare ZnO nanorods (with band-gap energy (Eg) of ∼3.28 eV) under visible light irradiation nor the nanorod heterostructures in dark exhibited any significant antibacterial activity, the ZnO@CdS nanorod heterostructures (with Eg ∼2.5-2.6 eV) could successfully inactivate the bacteria under visible light irradiation. Furthermore, it was found that an optimum loading of the CdS shell (corresponding to the effective thickness less than ∼15 nm) is required to achieve... 

We report a new design of solar cells based on semiconductor quantum dots (QDs), monolithic quantum dot sensitized solar cells (MQDSCs). MQDSCs offer the prospect of having lower cost and a simpler manufacturing process in comparison to conventional double substrate QDSCs. Our proposed monolithic QDSCs have a triple-layer structure, composed of a CdS sensitized mesoporous TiO2 photoanode, a scattering layer made by a core-shell structure of TiO 2/SiO2, and a carbon active/graphite counter electrode layer, which are all deposited on a single fluorine doped tin oxide (FTO) glass substrate. Mesoporous TiO2 was sensitized with CdS QDs by successive ionic layer adsorption and reaction. Here,... 

Cadmium sulfide (CdS) thin film was electrodeposited on indium tin oxide (ITO) by chronoamperometry. The SEM images showed that hexagonal sheets of CdS deposited on the ITO surface. The X-ray diffraction (XRD) analysis confirmed this structure for CdS crystals and the average of crystalline size and the lattice constant parameters are approximately 39.54 and a = 0.4136, c = 0.6696 nm respectively. Photo-electrochemical investigations were performed by cyclic voltammetry (CV), linear sweep voltammetry (LSV), and electrochemical impedance spectroscopy (EIS) techniques. CdS band edges and density of states (DOS) were determined by CV technique. The band gap energy (Ebg) was measured...