Interactions between the metal interconnect and glass sealant in the solid oxide cells stack are critical to retaining the system integrity. To address this issue, in the current study, 8YSZ coating is applied on the Crofer22 APU steel via sol-gel and dip-coating method. Dense and continuous 8YSZ coatings are obtained on Crofer22 APU substrates. X-ray diffraction and Raman spectroscopy results show that both cubic and tetragonal structures of 8YSZ are formed. A glass-based sealing paste is applied on bare and 8YSZ coated Crofer22 APU steel. The interfacial compatibility and chemical stability of steel/glass and steel/8YSZ/glass joint couples are investigated using SEM and EDS line scan... 

A pulsed Nd:YAG laser welding of 1 mm thick Ti (grade 2) to 0.5 mm thick AA3105-O was performed by a ring-like spot joining. A 0.15 mm thick Al-12Si-2.5 Mg alloy was used as a filler metal. Intermetallic compounds of Ti3Al, Ti2Al, TiAl, Ti(Al,Si)3 and Mg2Si were observed respectively from Ti towards Al sides at the fusion zone. Si and Mg increased the strength of the Al re-solidified zone near the Ti-Al interface because of their easy dissolution in the Al. Exothermic effect of the Mg addition resulted in porosity in the welding zone. Joint strength of up to 98% of the Al base metal was obtained, which was much 14% higher than that achieved by autogenous welding. © 2019 Elsevier GmbH  

In this study, a pulsed Nd:YAG laser welding method is implemented to join Ti-G2 (1 mm thick) to AA3105-O (0.5 mm thick) via a ring of spots filled with AlScZr alloy (0.15 mm thick). The filler material improved the weld’s microstructure and mechanical properties by reducing the undesirable intermetallic compounds (IMCs) such as TiAl2 and TiAl3 in the aluminium re-solidified zone near the titanium/aluminium interface. The joints having AlScZr filler were mostly failed at Al heat affected zone (HAZ) during the tensile shear test. The addition of zirconium to binary Al–Sc system formed a substitutional solid-solution in which 50 wt% Zr+10 wt% Ti replaced Al3(Sc,Zr,Ti). Scandium had a...